PVC CABLE COMPOUNDS

OUR PRODUCTS

Need Assistance?

+91-9848048646 elesvinyl@gmail.com
Contact us

PVC CABLE COMPOUNDS

  • - ELES PVC Compounds are specifically designed for Cables meeting various National & International standards. When correctly processed they offer short-term and long-term characteristics necessary to meet the mechanical, electrical and thermal requirements of these standards.

  • - Insulating, sheathing, jacketing high voltage, electronics, Tele-communication, data transfer, regular, heat/flame resistance, low temperatures - such requirements are met by specific grades of PVC Compounds developed at the in-house R&D centre.

  • - ELES PVC Compounds are convenient to process and ready to use.

  • - All special requirements of the PVC cable industry can be met by custom making the required quality products without affecting the prevailing marketconditions.

  • - Constant up-gradation in specifications for cables required by our esteemed customers.

ELES is geared to develop any special colour to meet specific requirements of customers, for the cable industry in particular.

TECHNICAL DATA

  • TYPE A : INSULATION GRADE

    Sl no PROPERTY UNIT Applicable standard IS-5831 EV 750 Values
    01 Hardness Shore A Not applicable 85
    02 Specific Gravity G/CC Not applicable 1.35 - 1.37
    03 Tensile Strength N/MM2 Min 12.5 14.2-5.5
    04 Elongation at Break % Min 150 190-250
    05 Thermal Stability Minutes Min 80 88-105
    06 Ageing in hot air Oven for (At 80° C/ 7 Days) ---------
    06(a) Variation of T.S % ±20 ±10
    06(b) Variation of elongation % ±20 ±15
    07 Loss of Mass Mg/cm2 Max 2 0.5 - 0.8
    08 Volume Resistivity Ohm-cm 1.0x1013 2.0x1013

    Notes :
    • - The specifications are subject to change with prior intimation.
    • - The properties have been tested on moulded sheet.
    • - The material to be kept in a cool and dry place.
    • - For smooth processing and better results, it is recommended to Pre-heat the material before use.
    • - The information provided is true to the best of our knowledge.
    • - The recommended processing temperature is 150-180°C.

  • TYPE C : HEAT RESISTANT COMPOUND 105°C

    Sl no PROPERTY UNIT Applicable IS-5831 Values for EV 600C
    01 Hardness Shore A Not applicable 95
    02 Specific Gravity G/CC Not applicable 1.38-1.40
    03 Thermal stability Minutes 100 130
    04 Volume Resistivity Ohm-cm 1.0x1013 10.0x1013
    05 Tensile Strength N/mm2 12.5 16.0-16.5
    06 Elongation at break % 125 200-220
    07 Ageing (135 °C for 7 days) ---------
    07(a) Variation in T.S % ±25 ±12
    07(b) Variation in Elongation % ±35 ±18

    Notes :
    • - The specifications are subject to change with prior intimation.
    • - The properties have been tested on moulded sheet.
    • - The material to be kept in a cool and dry place.
    • - For smooth processing and better results, it is recommended to Pre-heat the material before use.
    • - The information provided is true to the best of our knowledge.
    • - The recommended processing temperatures are 150-180°C.

  • TYPE : ST–1 CABLE SHEATHING GRADE

    Sl no PROPERTY UNIT Applicable IS-5831 Values for EV 850 S
    01 Hardness Shore A N.A 80-85
    02 Specific Gravity g/c.c N.A 1.35 - 1.38
    03 Tensile Strength N/mm2 Min 12.5 13.2-13.8
    04 Elongation at Break % Min 150 210 - 250
    05 Thermal Stability Minutes Min 40 60
    06 Loss of Mass Mg/cm2 Max 2 1
    07 Ageing (At 80° C For 7 Days) ---------
    07(a) Variation T. S % +20 +8
    07(b) Variation in Elongation % +20 +12

    Notes :
    • - The specifications are subject to change with prior intimation.
    • - The properties have been tested on moulded sheet.
    • - The material to be kept in a cool and dry place.
    • - For smooth processing and better results, it is recommended to Pre-heat the material before use.
    • - The information provided is true to the best of our knowledge.
    • - The recommended processing temperature is 150-180°C.

  • TYPE ST-2 : CABLE SHEATHING GRADE

    Sl no PROPERTY UNIT Applicable IS-5831 Values for EV 850 S
    01 Hardness Shore A N.A 90-95
    02 Specific Gravity g/c.c N.A 1.38-1.42
    03 Tensile Strength N/mm2 Min 12.5 14.5-15.0
    04 Elongation at Break % Min 150 200 - 205
    05 Thermal Stability Minutes Min 80 84-88
    06 Loss of Mass Mg/cm2 Max 2 1
    07 Ageing (At 100° C For 7 Days) ---------
    07(a) Variation T. S % +25 +7
    07(b) Variation in Elongation % +25 +10

    Notes :
    • - The specifications are subject to change with prior intimation.
    • - The properties have been tested on moulded sheet.
    • - The material to be kept in a cool and dry place.
    • - For smooth processing and better results, it is recommended to Pre-heat the material before use.
    • - The information provided is true to the best of our knowledge.
    • - The recommended processing temperature is 150-180°C.

  • TYPE : FRLS COMPOUNDS

    Sl no PROPERTY UNIT Applicable standards Specified Values Values for EV FRLS
    01 Hardness Shore A N.A N.A >100
    02 Specific Gravity g/c.c N.A N.A 1.56
    03 Tensile Strength N/mm2 IS-5831 Min 12.5 14.5
    04 Elongation at Break % IS-5831 Min 150 225
    05 Thermal Stability Minutes IS-5831 80 90
    06 Oxygen Index % ASTM Min 29 31
    07 Smoke Density % ASTM Max 60 25
    08 HCL Emission % IEC Max 20 16

    Notes :
    • - The specifications are subject to change with prior intimation.
    • - The properties have been tested on moulded sheet.
    • - The material to be kept in a cool and dry place.
    • - For smooth processing and better results, it is recommended to Pre-heat the material before use.
    • - The information provided is true to the best of our knowledge.
    • - The recommended processing temperature is 150-180°C.

  • TYPE : DF Grade

    Sl no PROPERTIES UNIT EV 1000 DF
    01 SPECIFIC GRAVITY G/CC 1.32+00.02
    02 SHORE HARDNESS Shore A 80-85
    03 TENSILE STRENGTH N/mm2 17.0-18.5
    04 ELONGATION % 320-360
    05 THERMAL STABILITY Minutes 42-45

    Notes :
    • - The specifications are subject to change with prior intimation.
    • - The properties have been tested on moulded sheet.
    • - The material to be kept in a cool and dry place.
    • - The information provided is true to the best of our knowledge. However, any liability in connection with data is disclaimed since the conditions of use are beyond our control.
    • - The recommended processing temperature are 110-120° C. However, the processing temperature etc. May be adjusted as per requirement for individual operations.

  • TYPE : Wire Coating Grade

    Sl no PROPERTIES UNIT EV 800 WC
    01 SPECIFIC GRAVITY G/CC 1.34+00.02
    02 SHORE HARDNESS Shore A 80-82
    03 TENSILE STRENGTH N/mm2 15.0-16.5
    04 ELONGATION % 250-280
    05 THERMAL STABILITY Minutes 82-85
    05 VOLUME RESISTIVITY OHM-CM 2X1013

    Notes :
    • - The specifications are subject to change with prior intimation.
    • - The properties have been tested on moulded sheet.
    • - The material to be kept in a cool and dry place.
    • - The information provided is true to the best of our knowledge. However, any liability in connection with data is disclaimed since the conditions of use are beyond our control.
    • - The recommended processing temperature is 175-185° C. However, the processing temperature etc. May be adjusted as per requirement for individual operations.
button